▎ 摘　　要

Natural fibers are now becoming widely adopted as reinforcements for polymer matrices to produce biodegradable and renewable composites. These natural composites have mechanical properties acceptable for use in many industrial and structural applications under ambient temperatures. However, there is still limited understanding regarding the mechanical performance of natural fiber composites when exposed to in-service elevated temperatures. Moreover, nanoparticle additives are widely utilized in reinforced composites as they can enhance mechanical, thermal, and physical performance. Therefore, this research extensively investigates the interlaminar shear strength (ILSS) and flexural properties of flax fiber composites with graphene at different weight percentages (0%, 0.5%, 1%, and 1.5%) and exposed to in-service elevated temperatures (20, 40, 60, 80, and 100 degrees C). Mechanical tests were conducted followed by microscopic observations to analyze the interphase between the flax fibers and epoxy resin. The results showed that a significant improvement in flexural strength, modulus, and interlaminar shear strength of the composites was achieved by adding 0.5% of graphene. Increasing the graphene to 1.0% and 1.5% gradually decreased the enhancement in the flexural and ILSS strength. SEM observations showed that voids caused by filler agglomeration were increasingly formed in the natural fiber reinforced composites with the increase in graphene addition.