▎ 摘　　要

Gold nanoparticle/graphene (GNP/GR) nanocomposite was one-pot synthesized from water soluble graphene and HAuCl4 by hydrothermal method and characterized by TEM, Raman spectroscopy, XRD, XPS, UV-vis spectroscopy, and electrochemical impedance spectroscopy (EIS). Electrogenerated chemiluminescence (ECL) of luminol was investigated at the GNP/GR modified glassy carbon electrode (GNP/GR/GCE) and the GNP modified glassy carbon electrode (GNP/GCE) in aqueous solution respectively. The results revealed that one strong anodic ECL peak could be observed at similar to 0.8 V at two modified electrodes compared with that at the bare electrode. The intensity of the anodic ECL at the GNP/GR/GCE is weaker than that at the GNP/GCE, which should be due to the synergic effect of the enhancing effect of gold nanopartides and the inhibiting effect of graphene on anodic luminol ECL. One strong cathodic ECL peak located at similar to-0.8 V could be observed at the GNP/GR/GCE but not at the GNP/GCE, which should be result from the adsorbed oxygen at the graphene film. In the presence of ascorbic acid, the anodic ECL at the GNP/GR/GCE was enhanced more than 8-times, which is more apparent than that at the GNP/GCE. Whereas, the cathodic ECL peak was seriously inhibited at the GNP/GR/GCE. The enhanced ECL intensity at the GNP/GR/GCE varied linearly with the logarithm of ascorbic acid concentration in the range of 1.0 x 10(-8) to 1.0 x 10-8 mol L-1 with a detection limit of 1.0 x 10(-9) MOIL-1. The possible ECL mechanism was also discussed. (C) 2014 Elsevier B.V. All rights reserved.