▎ 摘　　要

Predominant few-layer graphene (FLG) sheets of high electrical conductivity have been synthesized by a multi-step intercalation and reduction method. The electrical conductivity of the as-synthesized FLG is measured to be similar to 3.2 x 10(4) S m(-1), comparable to that of pristine graphite. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman analysis reveal that the as-synthesized FLG sheets have large areas with single and double layers. The specific capacitance of 180 F g(-1) is obtained for the FLG in a 1 M Na2SO4 aqueous electrolyte by integrating the cyclic voltammogram. The good capacitive behavior of the FLG is very promising for the application for next-generation high-performance electrochemical supercapacitors. (C) 2011 Elsevier B. V. All rights reserved.