▎ 摘　　要

This study reports on silicon nitride (Si3N4) and graphene nanoplatelets binary powder reinforced hybrid titanium composites obtained by a powder metallurgy method. Si3N4 powder was added at 3 wt.% and graphene nanoplatelets were added in various amounts (0.15, 0.30, 0.45, 0.60 wt.%) in the titanium matrix. Density, micro-Vickers hardness, compressive behavior, wear properties and microstructure of the hybrid composites were evaluated. Addition of different percentages of graphene nanoplatelets and 3 wt.% Si3N4 to the titanium matrix composites significantly enhanced mechanical properties. The highest hardness (634 HV) and compressive strength (1458 MPa) values were measured for 0.15 wt.% graphene nanoplatelets and 3 wt.% Si3N4 added titanium hybrid composite. The lowest mass loss and wear rate (Delta m = 4 mg, W = 6.1x10(-5) mm(3) (N m)(-1)) values were measured for the same 0.15 wt.% graphene nanoplatelets and 3 wt.% Si3N4 added titanium hybrid composite compared with pure Ti.