PurposeThis study aims to investigate the synergistic friction reduction and antiwear effects of lyophilized graphene loading nano-copper (RGO/Cu) as lubricating oil additives, compared with graphene. Design/methodology/approachThe friction performance of freeze-drying graphene (RGO) and RGO/Cu particles was investigated at different addition concentrations and under different conditions. FindingsGraphene plays a synergistic friction reduction and antiwear effect because of its large specific surface area, surface folds and loading capacity on the nanoparticles. The results showed that the average friction coefficients of RGO and RGO/Cu particles were 22.9% and 6.1% lower than that of base oil and RGO oil, respectively. In addition, the widths of wear scars were 62.3% and 55.3% lower than those of RGO/Cu particles, respectively. Originality/valueThe RGO single agent is suitable for medium-load and high-speed conditions, while the RGO/Cu particles can perform better in the conditions of heavy load and high speed.