▎ 摘　　要

TiC/graphene/Ti6Al4V composites were prepared by laser powder bed fusion using graphene and Ti6Al4V powder. The differences in microstructure and high-temperature mechanical properties between the Ti6Al4V alloy and the TiC/graphene/Ti6Al4V composite were studied. The tensile and microhardness of the two materials were tested at 400 degrees C, 500 degrees C, and 600 degrees C; the results of the TiC/graphene/Ti6Al4V composite were 126 MPa, 162 MPa, and 76 MPa and 70 HV, 59 HV, and 61HV, respectively, higher than those of the Ti6Al4V alloy. These results happened because graphene reacted with Ti to form TiC particles, which were homogeneously distributed amongst alpha' acicular martensite. The addition of graphene refined the size of the acicular alpha' martensite. At the same time, the graphene and TiC particles showed a dispersion-strengthening effect. The mechanical properties of the TiC/graphene/Ti6Al4V composite were improved by the combination of fine-grain strengthening and dispersion strengthening mechanisms.