▎ 摘　　要

Graphene oxide (GO) was modified by p-phenylenediamine (PPD), aiming at improving the wet-skid resistance and reduce the rolling loss of solution polymerized styrene-butadiene rubber (SSBR). PPD with amino groups enabled GO to obtain anti-aging function. The structure of modified GO (PPD-GO) was characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and Raman spectroscopy. Mechanical tests showed that the mechanical properties of SSBR before and after aging were improved by adding PPD-GO. The results of thermogravimetric-differential scanning calorimeter synchronization analysis (TGA-DSC) indicated that SSBR/PPD-GO obtained good thermo-oxidative stability. The dynamic mechanical analysis (DMA) of SSBR composites showed that the mechanical loss factor (tan delta) peak moved to high temperature with the content of PPD-GO. The tan delta values of SSBR composites showed that it had a good effect on improving the wet-skid resistance and reducing the rolling loss of SSBR by adjusting the content of PPD-GO. In particular, with the addition of 4 phr GO, SSBR was effectively improved in mechanical properties, aging resistance, wet-skid resistance and low rolling loss.