▎ 摘　　要

In the present study, graphene oxide (GO) was incorporated into poly(vinylidene fluoride) (PVDF) and chemically modified PVDF (M-PVDF) to prepare mixed matrix membranes (MMMs) for gas separation application. Performed analyses proved appropriate dispersion of exfoliated GO sheets in polymer matrices and sufficient compatibility at the interfacial phases. M-PVDF based MMMs were thermally and mechanically more stable relative to the PVDF-based MMMs. The oxygen containing functional groups in M-PVDF was probably the main reason for this more stability. PVDF/GO MMMs rendered low gas permeability and high selectivity. Both impermeable GO sheets and crystalline phases of PVDF were responsible for such behavior. On the other hand, interestingly gas permeability of M-PVDF/GO MMMs was enhanced while no substantial decline was recorded in gas selectivity. For instance, He and CO2 permeability was increased 12.46% and 25.89%, respectively, compared to the pure PVDF membrane. This behavior originated from functional groups of M-PVDF and the interaction of these groups with GO sheets. Since GO often amplified gas barrier properties of polymers, such increscent would be appreciable. (c) 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 46271.