▎ 摘　　要

Development of high-tapped-density graphene-based materials with satisfactory Brunauer-Emmett-Teller (BET) surface area can be beneficial to the optimization of the volumetric performance of supercapacitors for practical use. Herein, we report a simple and scalable route for the synthesis of high tapped-density N-doped graphene (HNG). The success of this work relies on the use of polyethyleneimine (PEI) to react with graphene oxide under ambient conditions to realize fast cross-linking and thus rapid sedimentation, followed by thermal treatment of the precipitates. The resultant HNG exhibits a good balance between the tapped density and BET surface area, where the tapped density can be tuned in the range of 0.90-1.20 g cm(3) and the BET surface area is maintained in the range of 457.0-119.6 m(2) g(-1). The interaction between PEI and graphene oxide successfully prevents restacking of the graphene layers during thermal treatment while allowing maximal volume shrinkage. When applied as an electrode material in supercapacitors, the HNG exhibits a volumetric capacitance up to 547.8 F cm(3) at a scan rate of 10 mV s(-1) and 317.3 F cm(3) at a current density 0.2 A g(-1), and it shows no apparent decrease in the specific capacitance after 5000 cycles at 2 A g(-1). The results demonstrate the feasibility of the new strategy for designing high-tapped-density graphene-based materials for supercapacitors. (C) 2017 Elsevier Ltd. All rights reserved.