• 文献标题:   Sustainable Microfabrication Enhancement of Graphene Nanoplatelet-Reinforced Biomedical Alumina Ceramic Matrix Nanocomposites
  • 文献类型:   Article
  • 作  者:   NASR MM, ANWAR S, ALSAMHAN AM, ALQAHTANI KN, DABWAN A, ALHAAG MH
  • 作者关键词:   al2o3 matrix nanocomposite, graphene nanoplatelet, clean sustainable manufacturing, highfrequency induction heating, laser micromachining performance, surface integrity
  • 出版物名称:   NANOMATERIALS
  • ISSN:  
  • 通讯作者地址:  
  • 被引频次:   0
  • DOI:   10.3390/nano13061032
  • 出版年:   2023

▎ 摘  要

Studies about adding graphene reinforcement to improve the microfabrication performance of alumina (Al2O3) ceramic materials are still too rare and incomplete to satisfy sustainable manufacturing requirements. Therefore, this study aims to develop a detailed understanding of the effect of graphene reinforcement to enhance the laser micromachining performance of Al2O3-based nanocomposites. To achieve this, high-density Al2O3 nanocomposite specimens were fabricated with 0 wt.%, 0.5 wt.%, 1 wt.%, 1.5 wt.%, and 2.5 wt.% graphene nanoplatelets (GNPs) using a high-frequency induction heating process. The specimens were subjected to laser micromachining. Afterward, the effects of the GNP contents on the ablation depth/width, surface morphology, surface roughness, and material removal rate were studied. The results indicate that the micro-fabrication performance of the nanocomposites was significantly affected by the GNP content. All nanocomposites exhibited improvement in the ablation depth and material removal rate compared to the base Al2O3 (0 wt.% GNP). For instance, at a higher scanning speed, the ablation depth was increased by a factor of 10 times for the GNP-reinforced specimens compared to the base Al2O3 nanocomposites. In addition, the MRRs were increased by 2134%, 2391%, 2915%, and 2427% for the 0.5 wt.%, 1 wt.%, 1.5 wt.%, and 2.5 wt.% GNP/Al2O3 nanocomposites, respectively, compared to the base Al2O3 specimens. Likewise, the surface roughness and surface morphology were considerably improved for all GNP/Al2O3 nanocomposite specimens compared to the base Al2O3. This is because the GNP reinforcement reduced the ablation threshold and increased the material removal efficiency by increasing the optical absorbance and thermal conductivity and reducing the grain size of the Al2O3 nanocomposites. Among the GNP/Al2O3 nanocomposites, the 0.5 wt.% and 1 wt.% GNP specimens showed superior performance with minimum defects in most laser micromachining conditions. Overall, the results show that the GNP-reinforced Al2O3 nanocomposites can be machined with high quality and a high production rate using a basic fiber laser system (20 Watts) with very low power consumption. This study shows huge potential for adding graphene to alumina ceramic-based materials to improve their machinability.