▎ 摘　　要

Liquid substrates are great candidates for the growth of high-quality graphene using chemical vapour deposition (CVD) due to their atomically flat and defect free surfaces. A detailed study of graphene growth using atmospheric pressure CVD (APCVD) on liquid indium (In) was conducted. It was found that the effect of the growth parameters on the quality of the graphene produced is highly dependent on the properties of the substrate used. A short residence time of 6.8 sec for the reactive gases led to a high graphene quality, indicating the good catalytic behaviour of In. The role of hydrogen partial pressure was found to be crucial, with monolayer and bilayer graphene films with a low defect density obtained at low P-H2 (38.6 mbar), whilst more defective, thicker graphene films with a partial coverage being obtained at high P-H2 (74.3 mbar). The graphene deposition was insensitive to growth time as the graphene growth on liquid In was found to self-limit to bilayer. For further investigation, five compositions of Cu-In alloys were made by arc-melting. Graphene was then grown using the optimum conditions for In and the quality of the graphene was found to degrade with increasing Cu wt.%. This work will aid the future optimisation of the growth conditions based upon the substrate's properties.