▎ 摘　　要

The intrinsic faradic reactivity is the uppermost factor determining the charge storage capability of battery material, the construction of p-n junction composing of different faradic components is a rational tactics to enhance the faradic activity. Herein, a reduced graphene oxide@cobalt nickle sulfide@nickle cobalt layered double hydroxide composite (rGO@CoNi2S4@NiCo LDH) with p-n junction structure is designed by deposition of n-type nickle cobalt layered double hydroxide (NiCo LDH) around p-type reduced graphene oxide@cobalt nickle sulfide (rGO@CoNi2S4), the charge redistribution across the p-n junction enables enhanced faradic activities of both components and further the overall charge storage capacity of the resultant rGO@CoNi2S4@NiCo LDH battery electrode. As expected, the rGO@CoNi2S4@NiCo LDH electrode can deliver high specific capacity (C-s, 1310 +/- 26 C g(-1) at 1 A g(-1)) and good cycleability (77% C-s maintaining ratio undergoes 5000 charge-discharge cycles). Furthermore, the hybrid supercapacitor (HSC) based on the rGO@CoNi2S4@NiCo LDH p-n junction battery electrode exports high energy density (E-cell, 57.4 Wh kg(-1) at 323 W kg(-1)) and good durability, showing the prospect of faradic p-n junction composite in battery typed energy storage. (C) 2021 Elsevier Inc. All rights reserved.