• 文献标题:   Growth and Characterization of Graphene on Polycrystalline SiC Substrate Using Heating by CO2 Laser Beam
  • 文献类型:   Article
  • 作  者:   GALVAO NKDM, DE VASCONCELOS G, DOS SANTOS MVR, CAMPOS TMB, PESSOA RS, GUERINO M, DJOUADI MA, MACIEL HS
  • 作者关键词:   polycrystalline sic, graphene, co2 laser heating, sic thermal decomposition, raman spectroscopy
  • 出版物名称:   MATERIALS RESEARCHIBEROAMERICAN JOURNAL OF MATERIALS
  • ISSN:   1516-1439 EI 1980-5373
  • 通讯作者地址:   Technol Inst Aeronaut
  • 被引频次:   5
  • DOI:   10.1590/1980-5373-MR-2016-0296
  • 出版年:   2016

▎ 摘  要

The thermal decomposition of silicon carbide (SiC), with the subsequent formation of graphene, can be achieved by heating treatment. Several heating processes have been applied for this purpose by using SiC, either in form of powder particles or monocrystalline substrate. In this work, instead of using an expensive commercially available SiC wafer, a polycrystalline SiC substrate was obtained, based on powder metallurgy process, in order to explore the synthesis of graphene layers on its surface by using a CO2 laser beam as heating source. Different levels of energy density (fluence) were applied and Raman spectroscopy analyses demonstrated that graphene layers were formed on the polycrystalline SiC surface. The ratio of the integrated intensity of the D and G bands, and the crystallite size were calculated. The FWHM of the 2D band peaks are in excellent agreement with the range of values found in the literature. The samples irradiated with energy density of 138.4 J/cm(2) presented lower concentration of defects and higher crystallite size, while the lowest FWHM was obtained for energy density of 188 J/cm(2). The process occurred at room conditions and no gas flow was used. The results reveal a simple and cost-effective alternative for synthesis of graphene-based structures on SiC.