▎ 摘　　要

The interest in wearable supercapacitors has been flourishing in both the scientific and industrial fields. Here, daily-used polyester fabric (PET) is modified by using an Al-based MOF, namely MIL-53(Al), via a layer-by-layer assembly method at room temperature. Then, reduced graphene oxide is deposited on the PET/MOF surface through dip coating in a graphene oxide suspension, followed by chemical reduction. Ultimately, pyrrole is polymerized on the surface of the PET/MOF/rGO surface by an in situ chemical polymerization process. The obtained composite is used as electrode achieving an areal capacitance of 510 mF cm(-2) at a scanning rate of 1 mV s(-1) in an aqueous H2SO4 electrolyte. The optimized electrode is employed in a symmetrical solid-state-supercapacitor device, which delivers a volumetric capacitance of 3.5 F cm(-3), energy density of 64 mu W h cm(-3) and power density of 0.6 mW cm(-3). The symmetrical device shows a good cycling stability even after 12 months storage in ambient conditions retained 85% of the initial capacitance after 1000 voltammetric cycles. (C) 2020 Elsevier Ltd. All rights reserved.