Metal organic frameworks (MOFs) with marvelous properties have aroused enormous attention for different application especially gas adsorption and separation. In this regard, fabrication of MOF hybrids with carbon based materials is new strategy to upgrade MOF performance. In this study CuBTC (Copper benzene-1,3,5-tricarboxylic acid)/graphene oxide (GO) composite was synthesized and characterized by BET, SEM, TGA, XRD and FT-IR techniques. Then CuBTC and CuBTC/GO composite were incorporated into polysulfone (PSF) polymer to construct mixed matrix membranes (MMMs). The obtained membranes were characterized by SEM, TGA, XRD and tensile tests and their gas permeability was measured. The results were compared to those of CuBTC/PSF MMMs. It was revealed that CuBTC/GO composite as filler showed superior performance relative to CuBTC. For instance, 15 wt% loading of CuBTC/GO in PSF represented outstanding gas separation behavior while the same loading of CuBTC in PSF deteriorated performance of MMM. Well particle dispersion and favorable polymer-filler interaction were responsible for such observed difference. A high H-2/CH4 and H-2/N-2 selectivity of 80.03 and 70.46 were recorded for CuBTC/GO in PSF (15 wt%) compared to 44.56 and 40.92 for CuBTC in PSF (15 wt%). (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.