▎ 摘　　要

The current global pandemic of new coronary pneumonia clearly reveals the importance of developing highly efficient filtration and fast germicidal performance of multifunctional air filters. In this study, a novel air filter with a controllable morphology based on the rod-like to flower-like zinc oxide/graphene-based photocatalytic composite particles loaded on glass microfiber was prepared by one-step microwave rapid synthesis. The multifunctional air filter shows the following special functions: the 10 mg.L-1 organic pollutant solution RhB was completely degraded within 2 h under a 500 W xenon lamp, and also 99% of Escherichia coli and Staphylococcus aureus were inactivated under a 60 W light-emitting diode lamp. Furthermore, after introducing the controllable morphology zinc oxide/graphene-based photocatalytic composite particles, the filtration efficiency of the multifunctional air filter was also kept at the same level (99.8%) as the one without any addition, indicating no loss of high-efficiency filtration while obtaining the rapid bactericidal function. The rapid antibacterial principle of the multifunctional air filter has also been proposed through the UV-vis spectroscopies, photoluminescence, and electron-spin resonance spectrum. The zinc oxide/graphene-based photocatalytic composite particles tightly coated on the glass microfiber surface could increase the active sites by changing the morphology of zinc oxide and, in the meantime, promote the separation of zinc oxide photo-generated electron-hole pairs to improve the rapid sterilization ability of the multifunctional air filters. In addition, an empirical formula to evaluate the relationship between the composition, viscosity, and viscosity modulus of glass microfiber was proposed by testing the viscosity of glass microfiber composed of 14 different compositions at 1300 and 1400 degrees C, which can be used as a criterion to evaluate the production technology of glass microfiber filters.