In industrial pollutants, phenol is a kind of degradation-resistant hazardous compound. It is generated during industrial processes in factories and treatment at sewage plants. In this study, we analyse the photocatalytic activity of TiO2 and rGO as a composite for the degradation of phenol. Hybridised titanium dioxide/reduced graphene oxide (TiO2/rGO) nanocomposites were synthesised by a simple hydrothermal method using flake graphite and tetrabutyl titanate as raw materials. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Brunauer-Emmet-Teller (BET) specific area analysis, Fourier transform infrared spectroscopy (FTIR), Raman, X-ray photoelectron spectroscopy (XPS), photoelectrochemical analysis, and UV-vis diffuse reflectance spectra (DRS) were employed to characterise the physicochemical properties of the as-prepared nanocomposites. The results showed the TiO2/rGO nanocomposites' significant anatase phase and a small fraction of the rutile phase the same as that of the as-prepared TiO2 nanoparticles. The spherical TiO2 nanoparticles (diameter 20-50 nm) were agglomerated slightly and the agglomerates were anchored on the rGO sheets and dispersed symmetrically. The specific surface area of TiO2/rGO-4% nanocomposites was 156.4 m(2)/g, revealing a high specific surface area. Oxygen-containing functional groups that existed in TiO2/rGO-4% nanocomposites were almost removed during hydrothermal processing. The photocurrent response of TiO2/rGO-4% was strongest among the TiO2/rGO nanocomposites, and the bandgap of TiO2/rGO-4% was 2.91 eV, showing a redshift of absorption into the visible region, which was in favour of the high photocatalytic activity of TiO2/rGO nanocomposites under visible light (lambda > 420 nm). Moreover, the samples were employed to photodegrade phenol solution under visible light irradiation. TiO2/rGO-4% nanocomposite degraded the phenol solution up to 97.9%, and its degradation rate constant was 0.0190 h(-1), which had higher degradation activity than that of other TiO2/rGO nanocomposites. This is a promising candidate catalyst material for organic wastewater treatment.