▎ 摘　　要

The progress in aerospace field requires a new NiAl matrix composite that can stand against wear and decrease the energy dissipation through decreasing friction. In this study, the tribological behavior of NiAl-1.5 wt% graphene composite is investigated at room temperature under a constant load of 12 N and different sliding velocities. The results show that the friction coefficient and wear rate increase with increasing sliding velocity from 0.2 to 0.4 m/s due to the adhesion between the sliding bodies and tearing of the graphene layer. The friction coefficient and wear rate tend to decrease at a sliding velocity of 0.6 m/s as a result of severe plastic deformation and grain refinement of the worn surface. However, at 0.8 m/s the friction coefficient reaches a minimum value and the wear rate increases and changes the wear mechanism to fatigue wear. It can be concluded that various wear mechanisms lead to different tribological performance of NiAl-1.5 wt% graphene composite.