▎ 摘　　要

Flexible organic solar cells (OSCs) composed of blended films of poly(3-hexylthiophene) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) were fabricated and investigated with chemically doped multilayer graphene films as transparent and conducting electrodes on plastic substrates. The sheet resistance of the chemically doped graphene film was reduced to half of its original value, resulting in a significant performance enhancement of OSCs featuring doped graphene electrodes. Moreover, there was no substantial variation observed in the fill factor and power conversion efficiency values of the flexible OSCs under bending conditions. A power conversion efficiency of similar to 2.5% for flexible OSCs with doped graphene electrodes was observed under bending conditions, even up to a 5.2 mm bending radius.