▎ 摘　　要

Graphene-based materials are promising electrodes for supercapacitors, owing to their unique two-dimensional structure, high surface area, remarkable chemical stability, and electrical conductivity. In this paper, graphene is explored as a platform for energy storage devices by decorating graphenes with flower-like MnO2 nanostructures fabricated by electrodeposition. The as-prepared graphene and MnO2, which were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM), have been assembled into an asymmetric supercapacitor. The specific capacitance of the graphene electrode reached 245 F/g at a charging current of 1 mA after an electro-activation process. This value is more than 60% larger than the one before electro-activation. The MnO2 nano-flowers which consisted of tiny rods with a thickness of less than 10 nm were coated onto the graphene electrodes by electrodeposition. The specific capacitance after the MnO2 deposition is 328 F/g at the charging current of 1 mA with an energy density of 11.4 Wh/kg and 25.8 kW/kg of power density. This work suggests that our graphene-based electrodes are a promising candidate for the high-performance energy storage devices. (C) 2011 Elsevier Ltd. All rights reserved.