▎ 摘　　要

Graphene nanoplatelets (GnP) and alpha-MnO2 decorated GnP were integrated into an ethylene vinyl acetate (EVA) matrix using the dual mixing method (solution followed by melt mixing). GnP was added in 1, 3, 5, 8, 10 and 15 phr loadings into an EVA matrix to obtain composites and evaluate their various properties suitable for mechanical and electrical applications. The graphene nanoplatelets were further decorated with alpha-MnO2 which was subsequently integrated into EVA at an 8 phr loading to form composites. It was observed in the GnP-EVA composites, that with an increasing GnP content, a substantial increase in the tensile strength (188%) over the neat polymer was observed at a 10 phr loading but reduced thereafter at a 15 phr loading. Dielectric permittivity of the composites were observed to increase with an increasing filler loading, the addition of a-Mn0 2 also having a beneficial effect. Conductivity as well as the electromagnetic interference shielding performance were improved with increasing GnP concentrations. A maximum 28 dB of shielding was observed in the 15 phr loaded GnP-EVA composite whereas the alpha-MnO2 decorated GnP-EVA composite showed a shielding efficiency of 22 dB at a concentration of 8 phr for a thickness of 2 mm with excellent thermal and mechanical properties. Overall, the composite material will find its application as a flexible EMI shielding material.