▎ 摘　　要

Graphene is considered an ideal lithium metal host material to suppress dendrite growth and buffer volume changes. Although defects on graphene are generally considered to enhance its lithiophilicity, defects that promote unstable solid electrolyte interphase (SEI) growth are rarely noticed. To explore which defect density of graphene is the most ideal host material, different defect densities of graphene are prepared as Li-metal host materials through thermal reduction at different temperatures (200 degrees C, 400 degrees C, 800 degrees C, 1200 degrees C, 1600 degrees C and 2200 degrees C). We are the first to demonstrate that molten lithium can spread into a graphene matrix with any density of defects and that Li2C2 is formed in less-defective 2200 degrees C rGO/Li anode. The 2200 degrees C rGO/Li composite anode exhibits the best electrochemical performance in all rGO/Li anodes, and the symmetrical cell with 2200 degrees C rGO/Li electrode shows stable cycling for 1200 h with a small polarization voltage of 12 mV at 1 mA cm(-2). Moreover, the 2200 degrees C rGO/Li parallel to S full cell displays stable cycling performance even with a high sulfur loading of 9.4 mg cm(-2); additionally, a high initial areal capacity of 9.7 mA h cm(-2) can be realized.