▎ 摘　　要

In this work, a graphene-decorated Li2S cathode has been prepared via spray drying method using Li2SO4, graphene oxide and sucrose as raw materials. During spray drying, sucrose melts and embeds Li2SO4 when Li2SO4 were sprayed out with graphene oxide and sucrose, and becomes sphere particles. The as-prepared Li2S composite was received after a heat treatment under nitrogen atmosphere. X-ray diffraction patterns confirm the cubic structure of Li2S and scanning electron microscope images reveal that Li2S and carbon components stay in sphere structure with diameter around 20m. The sphere Li2S composite shows enhanced performance when acts as cathode. Under current density of 100mAg(-1), a specific discharge capacity of 778mAhg(-1) has been achieved and the battery cycled over 60 rounds. Furtherly, the sphere composite was coupled with silicon/graphite anode to construct full cell system, suggesting large possibility to work with the current lithium-ion battery anodes.