▎ 摘　　要

This work is dedicated to the synthesis, characterization, and adsorption performance of reduced graphene oxide-modified spinel cobalt ferrite nanoparticles. The as-synthesized reduced graphene oxide cobalt ferrite (RGCF) nanocomposite has been characterized using FTIR spectroscopy, FESEM coupled with EDXS, XRD, HRTEM, zeta potential, and vibrating sample magnetometer (VSM) measurements. FESEM proves the particle size in the range of 10 nm. FESEM, EDX, TEM, FTIR, and XPS analyses provide the proof of successful incorporation of rGO sheets with cobalt ferrite nanoparticles. The crystallinity and spinel phase of cobalt ferrite nanoparticles have been shown by XRD results. The saturation magnetization (Ms) was measured as 23.62 emu/g, proving the superparamagnetic behavior of RGCF. The adsorption abilities of the synthesized nanocomposite have been tested using cationic crystal violet (CV) and brilliant green (BG) and anionic methyl orange (MO) and Congo red (CR) dyes. The adsorption trend for MO, CR, BG, and As(V) follows RGCF > rGO > CF at neutral pH. Adsorption studies have been accomplished by optimizing parameters like pH (2-8), adsorbent dose (1-3 mg/25 mL), initial concentration (10-200 mg/L), and contact time at constant room temperature (RT). To further investigate the sorption behavior, isotherm, kinetics, and thermodynamic studies have been conducted. Langmuir isotherm and pseudo-second-order kinetic models suited better for the adsorption of dyes and heavy metals. The maximum adsorption capacities (qm) obtained have been found as 1666.7, 1000, 416.6, and 222.2 mg/g for MO, CR, BG, and As, respectively, with operational parameters such as T = 298.15 K; RGCF dose: 1 mg for MO and 1.5 mg each for CR, BG, and As. Thus, the RGCF nanocomposite was found to be an excellent adsorbent for the removal of dyes and heavy metals.