▎ 摘　　要

We observed the coupling of graphene Dirac plasmons with different surfaces using scattering-type scanning near-field optical microscopy integrated into a mid-infrared synchrotron-based beamline. A systematic investigation of a graphene/hexagonal boron nitride (h-BN) heterostructure is carried out and compared with the well-known graphene/SiO2 heterostructure. Broadband infrared scanning nearfield optical microscopy imaging is able to distinguish between the graphene/h-BN and the graphene/SiO2 heterostructure as well as differentiate between graphene stacks with different numbers of layers. Based on synchrotron infrared nanospectroscopy experiments, we observe a coupling of surface plasmons of graphene and phonon polaritons of h-BN (SPPP). An enhancement of the optical band at 817 cm(-1) is observed at graphene/h-BN heterostructures as a result of hybridization between graphene plasmons and longitudinal optical phonons of h-BN. Furthermore, longitudinal optical h-BN modes are preserved on suspended graphene regions (bubbles) where the graphene sheet is tens of nanometers away from the surface while the amplitude of transverse optical h-BN modes decrease.