▎ 摘　　要

To explore aggregate-induced emission (AIE) properties, this study adopts a one-pot hydrothermal route for synthesizing polyethylene glycol (PEG)-coated graphene quantum dot (GQD) clusters, enabling the emission of highly intense photoluminescence under blue light illumination. The hydrothermal synthesis was performed at 300 degrees C using o-phenylenediamine as the nitrogen and carbon sources in the presence of PEG. Three different solvents, propylene glycol methyl ether acetate (PGMEA), ethanol, and water, were used for dispersing the PEG-coated GQDs, where extremely high fluorescent emission was achieved at 530-550 nm. It was shown that the quantum yield (QY) of PEG-coated GQD suspensions is strongly dependent on the solvent type. The pristine GQD suspension tends to be quenched (i.e., QY: similar to 1%) when dispersed in PGMEA (aggregation-caused quenching). However, coating GQD nanoparticles with polyethylene glycol results in substantial enhancement of the quantum yield. When investigating the photoluminescence emission from PEG-coated GQD clusters, the surface tension of the solvents was within the range of from 26.9 to 46.0 mN/m. This critical index can be tuned for assessing the transition point needed to activate the AIE mechanism which ultimately boosts the fluorescence intensity. The one-pot hydrothermal route established in this study can be adopted to engineer PEG-coated GQD clusters with solid-state PL emission capabilities, which are needed for next-generation optical, bio-sensing, and energy storage/conversion devices.