▎ 摘　　要

Reduced graphene oxide (rGO) modified graphitic carbon nitride (g-C3N4), CN/rGO, was synthesized as a modifier for porous polyethersulfone (PES) substrate for the preparation of thin film composite (TFC) polyamide forward osmosis (FO) membrane. The effect of CN/rGO addition on the PES substrate formation was investigated using viscosity and light transmittance measurements, and the PES-CN/rGO substrates and the FO membranes were characterized by SEM, TEM, AFM, XPS and contact angle measurements. The results indicated that the addition of CINI/rGO had a significant effect on the membrane properties. The FO membrane with an appropriate amount of CN/rGO in the PES substrate exhibited excellent FO performance. The osmotic water flux with 0.5 wt% CN/rGO in the substrate of TFC membrane reached 41.4 LMH using 2 M NaCl as draw solution and deionized water as feed, which was around 20% greater than with the control membrane without CN/rGO. The FO performance improvement should be attributed to the modified structure of the PES substrate, and thus lower structure parameter and the reduction of ICP. This study suggests that CN/rGO is an effective additive for modifying the porous substrate for the development of FO membranes. (C) 2014 Elsevier B.V. All rights reserved.