In order to improve the flame retardancy of glass fibers (GFs) reinforced polyamide 6 (PA6) composites and eliminate the "wicking effect," the preparation and application of graphene oxide (GO) modified GFs were investigated in this work. Flame retardant PA6 was prepared by blending graphene oxide modified GFs reinforced PA6 and aluminum diethyl phosphonate. For the GFs reinforced PA6, the limiting oxygen index of the composite increased from 20.6% to 22.3%, and peak heat release rate decreased by 37.2% in cone calorimeter test via introducing graphene oxide onto the surface of GFs. Comparing PA6/GF30/ADP15 and PA6/GF-GO30/ADP15, LOI of the later increased to 31.2%, the vertical burning test (UL-94) reached V-0, and the peak heat release rate decreased by 18.0%. The interface compatibility was greatly improved after the introduction of GO. The sheet structure of the GO on the GFs surface could block the combustible gas spillage and the flow of melt along the GFs, thus significantly attenuating the "wicking effect" and improving the flame retardancy of composites.