▎ 摘　　要

GO reinforced high-temperature titanium alloy matrix composite with excellent high-temperature strength and ductility was successfully fabricated by hot isostatic pressing and heat treatment. After solution and aging treatment, the high-temperature strength of the composite was significantly improved because the increase of in situ TiC at the interface enhanced interface bonding and the microstructure changed from equiaxed structure to bimodal structure. At the same time, the dissolution of silicides increased the high-temperature ductility. After solution at 1075 degrees C and aging at 700 degrees C, the tensile strength, yield strength and elongation at 600 degrees C of the high temperature titanium alloy with 0.3 wt% GO reached 749 MPa, 571 MPa and 18.5%, respectively.