▎ 摘　　要

Graphene oxide (GO) is one of the most important ceramic-toughening candidates due to its outstanding physical and chemical properties. In this paper, nacre-like alumina ceramics reinforced with GO have been prepared by freeze casting followed by hot pressing. The experimental results showed that a laminated structure with homogeneous distribution of GO was obtained in the composites. Microstructural analysis, relative densities, flexural strength and fracture toughness of the samples were investigated to reveal the effect of GO. Higher flexural strength and fracture toughness (similar to 380 MPa and similar to 7.5 MPa m(1/2), respectively) were achieved and the multiple length-scale toughening mechanisms of composites contributed to the improved mechanical properties. The results show that it is a promising method to enhance the mechanical properties of nacre-like alumina by the addition of GO.