▎ 摘　　要

Nitrogen-doped graphene oxide sheets (N-GOs) are prepared by employing N-containing polymers such as polypyrrole, polyaniline, and copolymer (polypyrrole-polyaniline) doped with acids such as HCl, H2SO4, and C6H5-SO3-K, which are activated using different concentrations of KOH and carbonized at 650 degrees C; characterized using SEM, TEM, BET, TGA-DSC, XRD, and XPS; and employed for the removal of environmental pollutant CO2. The porosity of the N-GOs obtained were found to be in the range 1-3.5 nm when the KOH employed was in the ratio of 1:4, and the XRD confirmed the formation of the layered like structure. However, when the KOH employed was in the ratio of 1:2, the pore diameter was found to be in the range of 50-200 nm. The SEM and TEM analysis reveal the porosity and sheet-like structure of the products obtained. The nitrogen-doped graphene oxide sheets (N-GOs) prepared by employing polypyrrole doped with C6H5-SO3-K were found to possess a high surface area of 2870 m(2)/g. The N-GOs displayed excellent CO2 capture property with the N-GOs; PPy/Ar-1 displayed similar to 1.36 mmol/g. The precursor employed, the dopant used, and the activation process were found to affect the adsorption property of the N-GOs obtained. The preparation procedure is simple and favourable for the synthesis of N-GOs for their application as adsorbents in greenhouse gas removal and capture.