▎ 摘　　要

Using an optimized KOH activation procedure we prepared highly porous graphene scaffoldmaterials with SSA values up to 3400m(2) g(-1) and a pore volume up to 2.2 cm(3) g(-1), which are among the highest for carbon materials. Hydrogen uptake of activated graphene samples was evaluated in a broad temperature interval (77-296 K). After additional activation by hydrogen annealing the maximal excess H-2 uptake of 7.5 wt% was obtained at 77 K. A hydrogen storage value as high as 4 wt% was observed already at 193 K (120 bar H-2), a temperature of solid CO2, which can be easily maintained using common industrial refrigeration methods.