▎ 摘　　要

In this paper, phosphorus graphene oxide/poly (vinyl alcohol) polymer (PGO/PVA polymer) was synthesized by PGO and PVA via the esterification in the case of faint acidity and the ultrasound irradiation and characterized; moreover, phosphorus graphene oxide/poly (vinyl alcohol) film (PGO/PVA film) was prepared by PGO/PVA polymer and characterized; also, the surface resistivity of PGO/PVA film was investigated in the case of the different amount of PGO. Based on those, it had been found that PGO reacted with PVA to produce PGO/PVA polymer via the esterification under the ultrasonic-assisted condition, and PGO/ PVA polymer was structured by 2D lattice of PGO and the chain of PVA connected in the form of six member lactone ring and phosphonic ester, and PGO/PVA film was constituted by PGO/PVA polymer, and surface resistivity of 0.00, 0.75, 1.50, 2.25 and 3.00 wt% of PGO/PVA film were 6.85 x 10(8), 2.98 x 10(8), 1.42 x 10(6), 7.66 x 10(4) and 1.29 x 10(5) Omega/sq, respectively. (C) 2016 Elsevier B.V. All rights reserved.