A novel water-induced shape memory nanocomposites were prepared by introducing graphene oxide (GO), which was based on microcrystalline cellulose nanofibers (MSF-g-COOH) extracting from sisal fibers. The results showed that the water-induced shape memory properties of MSF-g-COOH were significantly improved by the strong hydrogen bonding interaction between MSF-g-COOH and GO, It leads to some additional physically cross-linked points in MSF-g-COOH. On the other hand, at 0.5 wt% GO loading, tensile strength and Young modulus of the nanocomposite increased from 139 to 184 MPa, and from 5.77 to 8.54 GPa, respectively, compared to those of pure MSF-g-COOH. Furthermore, a water-induced model was proposed to discuss the water-induced shape memory behaviors of the MSF-g-COOH/GO nanocomposites. This study provides a framework for developing a cellulose based shape memory polymers (CSMPs) and better understanding the shape recovery mechanism in water-induced CSMPs.