▎ 摘　　要

Solvent-exfoliated graphene (SEG)-reinforced polystyrene (PS) composites were prepared using a straightforward solution-casting method. SEG sheets, obtained by sonication-assisted solvent direct exfoliation from natural graphite, were well dispersed in the PS matrix as evidenced from scanning electron microscopy and transmission electron microscopy observations. Addition of 0.5wt% SEG resulted in a 6% increase in tensile strength and a 77% improvement in Young's modulus over pure PS due to the effective load transfer between SEG and PS matrix. The Young's moduli of the PS/SEG composites were obtained from both tensile experiments and calculations using the well-established Halpin-Tsai model. Results from dynamic mechanical analysis indicated that the storage modulus of the PS/SEG composites was significantly improved relative to neat PS. The glass transition temperatures of the composites were found to increase substantially upon addition of SEG, consistent with differential scanning calorimetry analysis. (c) 2017 Society of Chemical Industry