▎ 摘　　要

Silicon is considered as one of the most promising anodes for Li-ion batteries (LIBs), but it is limited for commercial applications by the critical issue of large volume expansion during the lithiation. In this work, the structure of silicon/carbon (Si/C) particles on graphene sheets (Si/C-G) was obtained to solve the issue by using the void space of Si/C particles and graphene. Si/C-G material was from Si/PDA-GO that silicon particles was coated by polydopamine (PDA) and reacted with oxide graphene (GO). The Si/C-G material have good cycling performance as the stability of the structure during the lithiation/dislithiation. The Si/C-G anode materials exhibited high reversible capacity of 1910.5 mA h g(-1) and 1196.1 mA h g(-1) after 700 cycles at 357.9 mA g(-1), and have good rate property of 507.2 mA h g(-1) at high current density, showing significantly improved commercial viability of silicon electrodes in high-energy-density LIBs. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.