▎ 摘　　要

A graphene oxide aerogel (GOA) was formed inside a melamine sponge (MS) framework. After reduction with hydrazine at 60 degrees C, the electrical conductive nitrogen-enriched rGOA-MS composite material with a specific density of 20.1 mg/cm(3) was used to fabricate an electrode, which proved to be a promising electrocatalyst for the oxygen reduction reaction. The rGOA-MS composite material was characterized by elemental analysis, scanning electron microscopy, X-ray photoelectron spectroscopy, and Raman spectroscopy. It was found that nitrogen in the material is presented by different types with the maximum concentration of pyrrole-like nitrogen. By using Raman scattering it was established that the rGOA component of the material is graphene-like carbon with an average size of the sp(2)-domains of 5.7 nm. This explains a quite high conductivity of the composite obtained.