▎ 摘　　要

The objective of this work is to develop graphene oxide (GO) incorporated butyl rubber (IIR) nanocomposites by three different methods: direct addition approach (DAAM), single step method (SSM) and two step method (TSM). Chlorobutyl rubber was used as a compatibilizer in SSM and TSM. Mechanical properties of developed nanocomposites was increased and gas permeability co-efficient was decreasi up on addition of GO content in IIR matrix. Maximum technical properties was achieved for the nanocomposite with 1.6 wt.% of GO in all methods was achieved due to better interfacial bonding with IIR matrix. When GO content increases above 1.6 wt.% in RR matrix leads to agglomeration which resulted in deterioration of mechanical properties. HR-TEM studies revealed that nanocomposites prepared by TSM shows exfoliated structure of GO in IIR matrix due to homogenous distribution when compared to the nanocomposites prepared with DAAM and SSM.