Here in, we describe an ultrafast, single-step microwave irradiation route (MW) to prepare graphene supported Pt nanoparticles, during which the small Pt nanoparticles are distributed uniformly on a reduced graphene oxide surface. This route provides evident advantages namely low cost, easiness, low time consuming and high yield in comparison to actual chemical methods to develop efficient Pt/rGO catalyst with Pt content close to state-of-theart commercial composition. The structure and composition of prepared samples have been studied by specific techniques, while the electrocatalytic stability has been studied using ex situ and in-situ measurements. High performance and electrochemically stable catalyst for PEM fuel cells was developed using the sample with highest loading and good dispersion. The fabricated Pt-rGO-based MEA was investigated for durability under fuel starvation in comparison with commercial Pt/C-based MEA. The electrocatalytic activity was investigated and the electrochemical response revealed the higher stability during accelerated degradation test under fuel starvation in comparison with commercial Pt/C. This study promotes the applicability of described preparation method to noble or transition metal nanoparticles embedded on graphene-based materials. (c) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved. Here in, we describe an ultrafast, single-step microwave irradiation route (MW) to prepare graphene supported Pt nanoparticles, during which the small Pt nanoparticles are distributed uniformly on a reduced graphene oxide surface. This route provides evident advantages namely low cost, easiness, low time consuming and high yield in comparison to actual chemical methods to develop efficient Pt/rGO catalyst with Pt content close to state-of-theart commercial composition. The structure and composition of prepared samples have been studied by specific techniques, while the electrocatalytic stability has been studied using exsitu and in-situ measurements. High performance and electrochemically stable catalyst for PEM fuel cells was developed using the sample with highest loading and good dispersion. The fabricated Pt-rGO-based MEA was investigated for durability under fuel starvation in comparison with commercial Pt/C-based MEA. The electrocatalytic activity was investigated and the electrochemical response revealed the higher stability during accelerated degradation test under fuel starvation in comparison with commercial Pt/C. This study promotes the applicability of described preparation method to noble or transition metal nanoparticles