▎ 摘　　要

The synthesis of a composite of cobalt phosphide nanowires and reduced graphene oxide (denoted CoP/RGO) via a facile hydrothermal method combined with a subsequent annealing step is reported. The resulting composite presents large specific surface area and enhanced conductivity, which can effectively facilitate charge transport and accommodates variations in volume during the lithiation/de-lithiation processes. As a result, the CoP/RGO nanocomposite manifests a high reversible specific capacity of 960 mA center dot h center dot g(-1) over 200 cycles at a current density of 0.2 A center dot g(-1) (297 mA center dot h center dot g(-1) over 10,000 cycles at a current density of 20 A center dot g(-1)) and excellent rate capability (424 mA center dot h center dot g(-1) at a current density of 10 A center dot g(-1)).