• 文献标题:   Effect of a potassium promoter on the Fischer-Tropsch synthesis of light olefins over iron carbide catalysts encapsulated in graphene-like carbon
  • 文献类型:   Article
  • 作  者:   TIAN ZP, WANG CG, YUE J, ZHANG XH, MA LL
  • 作者关键词:  
  • 出版物名称:   CATALYSIS SCIENCE TECHNOLOGY
  • ISSN:   2044-4753 EI 2044-4761
  • 通讯作者地址:   Chinese Acad Sci
  • 被引频次:   11
  • DOI:   10.1039/c9cy00403c
  • 出版年:   2019

▎ 摘  要

Iron carbide catalysts encapsulated in graphene-like carbon were synthesized via a facile method by pyrolysis of an iron-glucose precursor. Different amounts of potassium (0-5 wt%) were in situ doped into the catalyst simultaneously. Glucose played a role both as the precursor to form a carbon support and a reducing agent that reduced iron oxides to.-Fe3C during the catalyst preparation..-Fe3C underwent a phase transformation to.-Fe5C2 as the active phase in Fischer-Tropsch synthesis. Characterization of the structural and chemical properties of the prepared catalysts revealed a core-shell structure with iron carbides enwrapped by several graphene-like layers. The addition of a potassium promoter increased the amount of defects on graphene-like layers and facilitated the formation of iron carbides during the catalyst preparation. Fischer-Tropsch synthesis under typical reaction conditions (320 degrees C, 20 bar, H2/CO = 1, GHSV = 15000 ml gcat(-1) h(-1)) was carried out in a fixed bed reactor. A higher light olefin selectivity was obtained than that on common iron catalysts, probably because of the electron-rich surfaces of the prepared catalysts that made it hard for hydrogen to hydrogenate the unsaturated intermediates. A volcano-like evolution of light olefin selectivity was observed on the catalysts with different contents of K, and the highest olefin selectivity reached 41.9% on the 2K-Fe3C@ C catalyst (i. e., doped with 2 wt% of K). The induction period of the catalyst was shortened by K addition. No drastic changes in the catalyst morphology and performance during 100 h time on stream can be ascribed to the protection of graphene-like carbon layers that prevented the supported iron particles from migration and aggregation under harsh conditions in FischerTropsch synthesis.