▎ 摘　　要

Mechanically strong, electrically conductive, and flexible pristine graphene-based composite paper was prepared based on heterocyclic aramid nanoparticle-assisted liquid-phase exfoliation of graphite. The macroscopic heterocyclic aramid yarns were split and assembled into heterocyclic aramid nanoparticles with the size of similar to 30 nm by deprotonation in dimethylsulfoxide in the presence of potassium hydroxide. The obtained heterocyclic aramid nanoparticles dimethylsulfoxide dispersion was used as good medium solvent for highly efficiency liquid-phase exfoliation of graphite. The results demonstrated that the concentration of exfoliated graphene can facile reaches similar to 2.72 mg/mL after direct sonication of 7 h with assist of heterocyclic aramid nanoparticles. After exfoliation, the self-assembled pristine graphene-based composite paper was fabricated by vacuum-assisted filtration. Due to the introduction of heterocyclic aramid nanoparticles, the self-assembled pristine graphene/heterocyclic aramid nanoparticles composite paper exhibited good mechanical property with tensile strength of similar to 129.7 MPa, meantime, has a high electrical conductivity of similar to 1.42 x 10(4) S/m.