▎ 摘　　要

Corrosion inhibition performances and adsorption behaviour at the aluminum-HCl solution interface were investigated for reduced graphene oxide nanosheets (rGONS), tetrakis-[4,4'-((4-(benzo[d]thiazol-2-yl)-1,2-bis(phenoxy)] (diphthalocyaninato gallium (III) chloride) (2) and tetrakis-4-(hexadecane-1,2-dioxyl)-bis(phthalocyaninato gallium(III) chloride) (1). Corrosion inhibition effects of rGONS, 1 and 2 were evaluated alone and in combination in 1.0 M hydrochloric acid solution using electrochemical techniques. The mechanism of aluminum corrosion inhibition revealed predominantly anodic character for rGONS and predominantly cathodic character for 1, 2, and conjugates with rGONS. The polarization technique gave inhibition efficiency values of 96.5% and 96.9% respectively for 1 and 2, which increased in the presence of rGONS to 97.4% and 98.1%, respectively, for the highest concentrations of 1 and 2. Scanning electron microscopy revealed effective metal surface protection by the inhibitors by formation of protective films. (C) 2021 Elsevier B.V. All rights reserved.