▎ 摘　　要

The formation of thin and uniform capacitive layers for fully interacting with an electrolyte in a supercapacitor is a key challenge to achieve optimal capacitance. Here, we demonstrate a binder-free and flexible supercapacitor with the electrode made of cobalt oxide nanoparticle (CoO NP)-wrapped graphene hollow nanoballs (GHBs). The growth process of Co(OH)(2) NPs, which could subsequently be thermally annealed to CoO NPs, was monitored by in situ electrochemical liquid transmission electron microscopy (TEM). In the dynamic growth of Co(OH)(2) NPs on a film of GHBs, the lateral formation of fan-shaped clusters of Co(OH)(2) NPs spread over the surface of GHBs was observed by in situ TEM. This CoO-GHBs/CC electrode exhibits high specific capacitance (2238 F g(-1) at 1 A g(-1)) and good rate capability (1170 F g(-1) at 15 A g(-1)). The outstanding capacitive performance and good rate capability of the CoO-GHBs/CC electrode were achieved by the synergistic combination of highly pseudocapacitive CoO and electrically conductive GHBs with large surface areas. A solid-state symmetric supercapacitor (SSC), with CoO-GHBs/CCs used for both positive and negative electrodes, exhibits high power density (6000 W kg(-1) at 8.2 Wh kg(-1)), high energy density (16 Wh kg(-1) at 800 W kg-1), cycling stability (similar to 100% capacitance retention after 5000 cycles), and excellent mechanical flexibility at various bending positions. Finally, a serial connection of four SSC devices can efficiently power a red light-emitting diode after being charged for 20 s, demonstrating the practical application of this CoO-GHBs/CC-based SSC device for efficient energy storage.