▎ 摘　　要

This report presents a facile and effective method to synthesize freestanding nitrogen-doped reduced graphene oxide (rGO)/activated carbon (AC) composite papers for supercapacitors by a method combining vacuum filtration with post-annealing in NH3 atmosphere. The effect of activated carbon contents on the microstructure and capacitive behavior of the resulting composite papers before and after the annealing was investigated by X-ray diffraction, scanning electron microscopy, and Raman and X-ray photoelectron spectroscopy. Results show that the composite paper with a 30% activated carbon loading has a high nitrogen content of 14.6 at% and superior capacitive performance (308 F/g, 1 A/g) to the other composite papers with various activated carbon loadings. Nitrogen was doped and GO reduced during the annealing. The rGO nanosheets acted as a framework, and the AC particles served as spacers to avoid agglomeration of graphene sheets. The high capacitance of the composite paper is ascribed to the electric double-layer behavior and the reversible redox reactions of the nitrogen and oxygen groups. The entire process is simple, environmental friendly and easily scalable for mass production.