▎ 摘　　要

Purpose The purpose of this study is to study the mechanical, tribological and electrical properties of the copper-graphene (Cu-Gn) composites fabricated by a novel rapid tooling technique consist of three-dimensional printing and ultrasonic-assisted pressureless sintering (UAPS). Design/methodology/approach Four different Cu-Gn compositions with 0.25, 0.5, 1 and 1.5 per cent of graphene were fabricated using an amalgamation of three-dimensional printing and UAPS. The polymer 3d printed parts were used to prepare mould cavity and later the UAPS process was used to sinter Cu-Gn powder to acquire free-form shape. The density, hardness, wear rate, coefficient of friction and electrical conductivity were evaluated for the different compositions of graphene and compared with the pure copper. Besides, the comparison was performed with the conventional method. Findings Cu-Gn composites revealed excellent wear properties due to higher hardness, and the lubrication provided by the graphene. The electrical conductivity of the fabricated Cu-Gn composites started increasing initially but decreased afterwards with increasing the content of graphene. The UAPS fabricated composites outperformed the conventional method manufactured samples with better properties such as density, hardness, wear rate, coefficient of friction and electrical conductivity due to homogeneous mixing of metal particles and graphene. Originality/value The fabrication of Cu-Gn composite freeform shapes was found to be difficult using conventional methods. The novel technique using a combination of polymer three-dimensional printing and UAPS as rapid tooling was introduced for the fabrication of freeform shapes of Cu-Gn composites and mechanical, tribological and electrical properties were studied. The method can be used to fabricate optimized complex Cu-Gn structures with improved wear and electrical applications.