Graphene oxide/polyurethane/epoxy resin nanocomposites containing various contents of graphene oxide were prepared by a sequential physical and polymeric technique. For the nanocomposites with a 0.3 mass% loading of graphene oxide, great improvement in tensile properties such as the elongation at break and toughness have been achieved by 45% and 87%, respectively. Meanwhile, the damping property of the nanocomposites is superior to that of the polyurethane/epoxy composite, with a 1 degrees C loss for the glass transition temperature. Combined with the morphology analysis, it has been proved that the polyurethane prepolymer terminated with hydroxyl groups and graphene oxide exhibit synergistic effect on improving mechanical properties of neat epoxy resin.