▎ 摘　　要

Herein, we report a successful synthesis of supramolecularly assembled polyaniline/silver oxide/graphene oxide composite (PANI/Ag2O/GO) for enhanced NO2 gas sensing application. The PANI/Ag2O/GO composite was synthesized by facile stirring followed by an ultrasonication process. The prepared material was characterized by different techniques such as x-ray diffraction, field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectroscopy and Raman-scattering spectroscopy. The detailed analysis revealed that the average crystallite sizes of PANI/Ag2O and PANI/Ag2O/GO composites were found to be 37.37 nm and 41.55 nm, respectively. FESEM and TEM analysis showed coral-like roughsurfaced and extensively agglomerated morphology for PANI and ultrathin flexible sheet-like morphology for GO. Ag2O nanoparticles with diameters 20-30 nm were well incorporated in the GO sheets and PANI matrix in the case of PANI/Ag2O/GO composites. The synthesized materials were used to make resistive sensor devices that had a high response to NO2 gas. The fabricated sensors were examined at various temperatures to obtain the optimal sensing temperature. The fabricated NO2 gas sensor device based on PANI/Ag2O/GO composite exhibited a highest sensitivity of 5.85 for 25 ppm at an optimized temperature (100 degrees C) as compared to the pure PANI (2.5) and PANI/Ag2O composite (3.25). Further, the fabricated sensor device based on PANI/Ag2O/GO composite was also examined at different NO2 gas concentrations.