▎ 摘　　要

Reactivity is of great importance for metal oxide nanoparticles (MONP) used as catalysts and advanced materials, but seeking for higher reactivity seems to be conflict with high chemical stability required for MONP. There is direct balance between reactivity and stability of these MONP. This could be acheived for metal oxide by dispersing them in a substrate. Here, we report a simple, efficient and high-yield process for the production of copper oxide (CuO) nanoparticles dispersed on a chemically inert material, few layer hexagonal boron nitride (h-BN) with a thickness around 1.7 nm and lateral dimensions mostly below 200 nm. The mechano-chemical reaction which take place at atmospheric pressure and room temperature involves a urea assisted exfoliation of pristine boron nitride. Copper oxide nanoparticles dispersed on the surface of these few layered h-BN reduced its tendency for aggregation. The optimum concentration of CuO:h-BN was found to be 2:1 which shows highest catalytic activity for the thermal decomposition of ammonium perchlorate. The high catalytic activity of the in situ synthesized CuO-hBN composite may be attributed to uniform distribution of CuO nanoparticles on the few layered h-BN which in turn provide a number of active sites on the surface due to non aggregation. (C)2017 Elsevier Inc. All rights reserved.