• 文献标题:   High toughness Si3N4 ceramic composites synergistically toughened by multilayer graphene/beta-Si3N4 whisker: Preparation and toughening mechanism investigation
  • 文献类型:   Article
  • 作  者:   CHEN F, YAN K, ZHOU JP, ZHU YS, HONG J
  • 作者关键词:   graphene, orthogonal experiment, si3n4 whisker, mechanical propertie
  • 出版物名称:   JOURNAL OF ALLOYS COMPOUNDS
  • ISSN:   0925-8388 EI 1873-4669
  • 通讯作者地址:  
  • 被引频次:   4
  • DOI:   10.1016/j.jallcom.2022.166183 EA JUL 2022
  • 出版年:   2022

▎ 摘  要

This work aimed at investigating the superiorities of multilayer graphene (MLG) and beta-Si3N4 whisker (beta-Si3N4w) in synergistically enhancing the toughness of Si3N4 ceramic composites. First, Si3N4 ceramic composites with hybrid 1 wt% MLG and 0 - 5 wt% beta-Si3N4w were sintered by spark plasma sintering. Phase constitutions and microstructures of Si3N4-based ceramic composites were characterized by X-rays dif-fraction, Raman spectra, and scanning electron microscope. Then, the optimal beta-Si3N4w content and sin-tering process of MLG/beta-Si3N4w-toughened Si3N4 ceramic composites were comprehensively optimized by orthogonal experiments. Results indicated that in the case of maintaining the hardness of 15.87 - 18.84 GPa, the fracture toughness of Si3N4 ceramic composites incorporated with 1 wt% MLG and 3 wt% beta-Si3N4w was advanced to 11.04 MPa.m(1/2), which was 11.29% and 87.12% higher than that of 1 wt% MLG- and 3 wt% beta-Si3N4w-reinforced Si3N4 ceramic composites, respectively. Orthogonal experiments demonstrated that 1 wt % MLG/3 wt% beta-Si3N4w-toughened Si3N4 ceramic composites sintered at 1600 degrees C, 40 MPa, and holding time for 6 min had optimum comprehensive mechanical properties. MLG wrapping and the synergistic effects of pull out, crack deflection, crack branching, and bridging resulted by MLG and beta-Si3N4w were the main responsible for the enhancement of toughness. (C) 2022 Elsevier B.V. All rights reserved.